Effect of Nano Filled Protective Coating and Dentin Bonding Agent on the Microleakage Resistance of A Hybrid Composite During Bleaching Treatment- An In Vitro Study

Rashi Motwani, BDS,MDS.1*| Savarna Goswami, BDS,MDS1*| Anu Narang, BDS,MDS1*| Santhosh Kumar Singh, BDS,MDS1*| Suchi Pandey, BDS,MDS1*| Muskan Sitlani, BDS,MDS1*

1 Department of Conservative Dentistry and Endodontics, Peoples College of Dental Sciences and Research Centre Bhopal-460237, Madhya Pradesh, India

Correspondence

Dr.RashiMotwani,

Post-graduate student, Department of Conservative Dentistry and Endodontics, Peoples College of Dental Sciences and Research Centre Bhopal-460237, Madhya Pradesh, India

Email:r26motwani@gmail.com

Abstract

Activation of bleaching agents containing hydrogen peroxide or carbamide peroxide results in their transformation into low molecular weight reactive free radicals which infiltrate dental hard tissues. These, in turn, remove the discolouration in the dental tissue. However, they may have undesired consequences on the dental tissues, restoration materials, and tooth restoration interfaces. Microleakage at restoration margins is a significant consequence which can lead to numerous clinical issues. Some of these are pulpal damage, secondary caries, surgical sensitivity, marginal discolouration, and bacterial buildup. Surface coating agents or protective coating materials can be considered as an alternative for minimizing microleakage, to prevent these clinical adverse effects. The materials are applied to the cavosurface margins of completed restorations, where they penetrate into structural microdefects and marginal gaps formed during the finishing and polishing operations via capillary action. This study examined the effects of a nanoparticle-loaded covering material on the hybrid composite resin's marginal integrity after bleaching. Class V cavities were created in the middle third of human premolar buccal surfaces and were restored with hybrid composite resin for three groups (n = 30). Group A-restored and coated with G coat plus and bleached using 35 % H2O2 . Group B-restored and coated with dentin bonding agent & bleached using 35 % H2O2. Group C-restored with hybrid composite resin, without any coating \& was bleached using H2O2.  All specimens were dyed with 0.5 % fuschin stain & observed under the stereomicroscope for assessing the marginal gap and microleakage. Group A showed maximum resistance to microleakage in this study.

Acknowledgments

Nil

Conflict of interest

The authors have no conflicts of interest to declare

How to cite this article: Motwani R, Goswami S, Narang A, Singh SK, Pandey S, Sitlani M. Effect of Nano Filled Protective Coating and Dentin Bond-ing Agentonthe Microleakage Resistance of AHy-brid Composite During BleachingTreatment-An In Vitro Study. IntJ OrofacRes.2024;8(1):11-16.https://doi.org/10.56501/intjorofacres.v8i1.992

Previous
Previous

Case Report

Next
Next

Case Report